Effect of anatase TiO2 nanoparticles on the growth of RSC-364 rat synovial cell.

Effect of anatase TiO2 nanoparticles on the growth of RSC-364 rat synovial cell.

Journal of nanoscience and nanotechnology (2013-07-19)

Jiangxue Wang, Jiawei Ma, Linmeng Dong, Ying Hou, Xiaoling Jia, Xufeng Niu, Yubo Fan

ABSTRACT

Nanoscale materials (such as TiO2, hydroxyapatite nanoparticles) have gained much concern in the coating of implants for cell adhesion and growth to improve the osteoconductivity. However, due to attrition and corrosion, the wear particles would be generated from the joint in living organism, and influence the physiological function of synovial membranes in joint cavity. In this study, the potential cytotoxicity of anatase TiO2 nanoparticles (TiO2 NPs) on rat synovial cell line 364 (RSC-364) was investigated. After treatment with different concentrations of TiO2 NPs (0, 3, 30, 300 microg/ml), the viability of RSC-364 cells were decreased in a dose-dependent manner. TiO2 NPs exposure could disrupt the integrity of cell plasma membrane, leading to the increased leakage of lactate dehydrogenase (LDH) into the culture medium. TiO2 NPs were uptaken by RSC-364 cells. The ultrastructure of RSC-364 cells was changed such as nuclear shrinkage and mitochondrial swelling. The reactive oxygen species (ROS) was over-produced especially in the cells exposed to 30 and 300 microg/ml TiO2 NPs. The activities of endogeneous antioxidant enzymes, superoxide dismutase (SOD) and catalase (CAT), were significantly decreased. The increased lipid peroxidation product (malondialdehyde, MDA) suggests the oxidative damage in cells. The flow cytometry detected that the cell cycle was blocked in G0/G1 phase, inhibiting the cell proliferation. These preliminary results indicate the oxidative stress injury and cytotoxicity of anatase TiO2 NPs on rat synovial cells. The reasonable and safe application of nanomaterials in artificial implants needs further study.

MATERIALS

Product Number

Brand

Product Description

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

305812

Sigma-Aldrich

Titanium, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

718467

Sigma-Aldrich

Titanium(IV) oxide, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

30-2730

Sigma-Aldrich

Titanium(IV) oxide, JIS special grade, ≥99.0%

637254

Sigma-Aldrich

Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

433667

Sigma-Aldrich

Titanium, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

IRMM531A

Titanium, IRMM^®, certified reference material, 0.1 mm foil

460397

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, ≥99.99% trace metals basis

348805

Sigma-Aldrich

Titanium, foil, thickness 0.5 mm, 99.99% trace metals basis

268496

Sigma-Aldrich

Titanium, powder, −100 mesh, 99.7% trace metals basis

366994

Sigma-Aldrich

Titanium, powder, <45 μm avg. part. size, 99.98% trace metals basis

267481

Sigma-Aldrich

Titanium, foil, thickness 0.25 mm, 99.99% trace metals basis

232033

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, 99.8% trace metals basis

677469

Sigma-Aldrich

Titanium(IV) oxide, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

248576

Sigma-Aldrich

Titanium(IV) oxide, anatase, powder, −325 mesh, ≥99% trace metals basis

767506

Sigma-Aldrich

Titanium, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis