Design and fabrication of carbon quantum dots/TiO2 photonic crystal complex with enhanced photocatalytic activity.

Design and fabrication of carbon quantum dots/TiO2 photonic crystal complex with enhanced photocatalytic activity.

Journal of nanoscience and nanotechnology (2014-04-18)

Zhong Huang, Liang Fang, Wen Dong, Yang Liu, Zhenhui Kang

ABSTRACT

TiO2 photonic crystal photocatalyst with inverse opal structure were first prepared from self-assembled polystyrene spheres template, and then carbon quantum dots (CQDs) was coupled with TiO2 inverse opal through a facile electrodeposition method. The obtained CQDs/TiO2 complex photocatalysts exhibit enhanced photocatalytic activity compared to pure TiO2 inverse opal, especially under the irradiation of visible light. Our results provide a promising methodology for designing high performance photocatalysts based on photonic crystal and CQDs, which is benefit for catalytic and new energy applications.

MATERIALS

Product Number

Brand

Product Description

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

305812

Sigma-Aldrich

Titanium, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

GF65336700

Titanium, rod, 200mm, diameter 2mm, annealed, 99.6+%

GF76772391

Titanium, rod, 100mm, diameter 10mm, annealed, 99.6+%

GF87716997

Titanium, rod, 100mm, diameter 16mm, as drawn, 99.99+%

GF06082286

Titanium, microfoil, disks, 10mm, thinness 1.0μm, specific density 429μg/cm², permanent mylar 3.5μm support, 99.6+%

GF03916290

Titanium, rod, 490mm, diameter 2mm, annealed, 99.6+%

GF68670366

Titanium, tube, 1220mm, outside diameter 2.03mm, inside diameter 1.55mm, wall thickness 0.24mm, annealed, 99.6+%

GF82517722

Titanium, tube, 1000mm, outside diameter 6.35mm, inside diameter 4.57mm, wall thickness 0.89mm, annealed, 99.6+%

GF50171318

Titanium, rod, 25mm, diameter 16mm, as drawn, 99.99+%

GF03838282

Titanium, rod, 500mm, diameter 1.5mm, annealed, 99.6+%

GF04311638

Titanium, rod, 100mm, diameter 6mm, annealed, 99.6+%

GF25290581

Titanium, tube, 1000mm, outside diameter 25.4mm, inside diameter 23.62mm, wall thickness 0.89mm, annealed, 99.6+%

GF20882998

Titanium, rod, 200mm, diameter 5mm, annealed, 99.6+%

GF65694426

Titanium, tube, 100mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF16031843

Titanium, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave