Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Functionalized bio-artifact fabricated via selective slurry extrusion. Part 2: Fabrication of ceramic dental crown.

Journal of nanoscience and nanotechnology (2014-04-17)

D B Zhu, J P Liang, Y X Qu, G L Duan

要旨

Functionalized ceramic dental crown was successfully fabricated through selective slurry extrusion (SSE) based technique of solid freeform fabrication (also known as rapid prototyping). After sintering, the decomposed tourmaline powders were embedded in ZrO2 matrix. The far infrared emission properties of the ceramic dental crown were improved due to the increase of the numbers of infrared active bonds from tourmaline. This new dental restoration process presents potential to provide dental patients with functionalized artificial teeth, which benefits the body health by the way of emitting far infrared rays in ambient temperatures.

材料

製品番号

ブランド

製品内容

Sigma-Aldrich

酸化ジルコニウム(IV), powder, 5 μm, 99% trace metals basis

Sigma-Aldrich

酸化ジルコニウム(IV), nanopowder, <100 nm particle size (TEM)

Sigma-Aldrich

ジルコニウム, powder, −100 mesh

Sigma-Aldrich

酸化ジルコニウム(IV), 99.99% trace metals basis (purity excludes ~2% HfO₂)

Sigma-Aldrich

ジルコニウム, foil, thickness 0.1 mm, 99.98% trace metals basis

Sigma-Aldrich

ジルコニウム, rod, diam. 6.35 mm, ≥99% trace metals basis

Sigma-Aldrich

ジルコニウム, sponge, ≥99% trace metals basis

Sigma-Aldrich

酸化ジルコニウム(IV)分散液, nanoparticles, dispersion, <100 nm particle size (BET), 10 wt. % in H₂O

Sigma-Aldrich

酸化ジルコニウム(IV)分散液, nanoparticles, dispersion, <100 nm particle size (BET), 5 wt. % in H₂O

ジルコニウム, foil, light tested, 150x150mm, thickness 0.05mm, annealed, 99.2%

ジルコニウム, sponge, 500g, max. size 25mm, 99.2%

ジルコニウム, rod, 100mm, diameter 1.5mm, 99.2%

ジルコニウム, rod, 500mm, diameter 1.5mm, 99.2%

ジルコニウム, foil, 150x150mm, thickness 0.5mm, annealed, 99.2%

ジルコニウム, foil, light tested, 100x100mm, thickness 0.025mm, annealed, 99.2%

ジルコニウム, foil, 25x25mm, thickness 2.0mm, annealed, 99.2%

ジルコニウム, rod, 1000mm, diameter 1.5mm, 99.2%

ジルコニウム, foil, 0.5m coil, thickness 0.5mm, annealed, 99.2%

ジルコニウム, foil, light tested, 25x25mm, thickness 0.05mm, annealed, 99.2%

ジルコニウム, rod, 200mm, diameter 1.5mm, 99.2%

ジルコニウム, rod, 100mm, diameter 2.0mm, centerless ground, 99.2%

ジルコニウム, rod, 500mm, diameter 2.0mm, centerless ground, 99.2%

ジルコニウム, foil, 100x100mm, thickness 0.5mm, annealed, 99.2%

ジルコニウム, foil, light tested, 100x100mm, thickness 0.05mm, annealed, 99.2%

ジルコニウム, sponge, 100g, max. size 25mm, 99.2%

ジルコニウム, foil, 10mm disks, thickness 0.01mm, 99.2%

ジルコニウム, sponge, 50g, max. size 25mm, 99.2%

ジルコニウム, foil, light tested, 25x25mm, thickness 0.016mm, 99.2%

ジルコニウム, foil, light tested, 25x25mm, thickness 0.01mm, 99.2%

ジルコニウム, foil, light tested, 25x25mm, thickness 0.02mm, 99.2%