934739

Sodium manganese oxide

electrode sheet, aluminum substrate, size 5 in. × 10 in.

• 別名: Manganese oxide cathode, Sodium-ion battery cathode
• 実験式（ヒル表記法）: Na_0.44MnO₂
• 分子量: 97.05
• UNSPSCコード: 26111700
• NACRES: NA.21

特性

• 物質: aluminum substrate
• 品質水準: 100
• グレード: battery grade
• 詳細: 2.5 V vs Na/Na⁺; Application: Battery Manufacturing
• アッセイ: ≥98%
• フォーム: sheet
• 組成: Active material loading 8.6 mg/cm² ± 5%
• 環境により配慮した代替製品の特徴: Design for Energy Efficiency; Learn more about the Principles of Green Chemistry.
• sustainability: Greener Alternative Product
• サイズ: 5 in. × 10 in.
• 厚さ: 16 μm , aluminum current collector; 25-50 μm ; 72-80 μm , excluding current collector
• 粒径: 1-2 μm (active material characteristic)
• キャパシティ: 0.90 mAh/cm2±5 % (Areal capacity)
• アプリケーション: battery manufacturing
• 環境により配慮した代替製品カテゴリ: Enabling

詳細

詳細

Sodium manganese oxide (Na_0.44MnO₂) electrode sheet is a ready-to-use cathode for sodium-ion battery research. The film is 5 inches x 10 inches (127 mm x 254 mm) and cast single-sided on a 16 µm thick aluminum foil current collector. The composition is 90% sodium manganese oxide (Na_0.44MnO₂), 5% Poly(vinylidene fluoride) [PVDF] and 5% carbon black. The active material is tunnel-type sodium manganese oxide, which offers fast sodium ionic conductivity and high chemical stability. PVDF acts as binder due to its thermal and electrochemical stability and carbon black boosts the electronic conductivity.

We are committed to bringing you Greener Alternative Products, which adhere to one or more of The 12 Principles of Greener Chemistry. This product has been enhanced for energy efficiency. Click here for more information.

アプリケーション

The primary application of our sodium manganese oxide (Na_0.44MnO₂) electrode sheet is as a cathode for sodium-ion battery research. Manganese-based compounds are widely investigated as cathode materials for rechargeable Na-ion batteries and, in particular, tunnel-type sodium manganese oxide (Na_0.44MnO₂₎ is a promising cathode material due to its high capacity, low cost, and non-toxicity. In addition, its unique tunnel structure facilitates excellent cycle and rate performance. For example, our sodium manganese oxide showed a large capacity (experimentally 110 mAh g−1 at 0.1C), even at fast charge rates (80 mAh g-1 at 5C, 72%). In addition, Na_0.44MnO₂ shows excellent stability with a variety of electrolytes including NaClO₄ and NaPF6-based organic electrolytes.